一、陶瓷耐磨試驗機用了擺線針輪減速機，減速比大，結(jié)構(gòu)緊湊，傳動平穩(wěn)，磨料流量可調(diào)，能有效地節(jié)約磨料的用量。該試驗機通過齒輪傳動減速達(dá)到鋼輪轉(zhuǎn)速75r/min，齒輪傳動相比皮帶傳動減速**、平穩(wěn)、不會出現(xiàn)打滑現(xiàn)象，鋼輪轉(zhuǎn)動由時間繼電器控制，電機轉(zhuǎn)到預(yù)定時間也**是轉(zhuǎn)到試驗要求的轉(zhuǎn)速，電機自動停止。鋼輪式耐磨試驗機，陶瓷磚耐磨試驗機本機適用于無釉磚、馬賽克、水泥路面磚等脆性材料的耐磨試驗，是為完善建筑陶瓷及配件生產(chǎn)企業(yè)的檢驗條件，提高檢測水平，確保產(chǎn)品質(zhì)量**的檢驗用儀器設(shè)備之一。
First, the ceramic wear tester uses a cycloid pinwheel reducer, which has a large reduction ratio, a compact structure, a stable transmission, and an adjustable abrasive flow rate, which can effectively save the amount of abrasive. The test machine reduces the speed of the steel wheel to 75r / min through gear transmission. Compared with belt transmission, the gear transmission is slower, smoother, and no slippage occurs. The rotation of the steel wheel is controlled by the time relay, and the motor is turned to the predetermined time. Turn to the speed required by the test and the motor will automatically stop. Steel wheel abrasion tester, ceramic tile abrasion tester This machine is suitable for abrasion test of brittle materials such as unglazed tiles, mosaics, and cement pavement tiles. Level, one of the inspection equipment to ensure product quality
二、陶瓷耐磨試驗機具有設(shè)計合理、結(jié)構(gòu)簡單、造型美觀、操作方便、轉(zhuǎn)動平穩(wěn)，達(dá)到試驗要求自動停機等特點，主要適用用于水泥磚的耐磨試驗。
Second, the ceramic abrasion tester has the characteristics of reasonable design, simple structure, beautiful appearance, convenient operation, smooth rotation, automatic shutdown when it meets the test requirements, and is mainly used for abrasion test of cement bricks.
三、陶瓷耐磨試驗機符合標(biāo)準(zhǔn)：
GB/T3810.7—2016《無釉磚耐磨試驗方法》
ISO/DIS10545/6—94《無釉磚耐深度磨損試驗方法》
GB/T12988-1009《無機地面材料耐磨試驗方法》
Third, the ceramic wear tester meets the standards:
GB / T3810.7—2016 "Abrasion Test Method for Unglazed Bricks"
ISO / DIS10545 / 6-94 "Test Method for Deep Wear Resistance of Unglazed Bricks"
GB / T12988-1009 "Test method for abrasion resistance of inorganic floor materials"
四、陶瓷耐磨試驗機技術(shù)參數(shù)：
●磨輪一：直徑200±0.2mm，厚度10±0.1mm，
●磨輪二：直徑200±0.2mm，厚度70±0.1mm，硬度HB203-245
●磨輪轉(zhuǎn)速：75±4r/min恒定；
●試樣尺寸：100mm ×110 mm；
●磨料：粒度為ISO8486-1986中規(guī)定的F80白色熔融氧化鋁；
●磨料給入速度：（100±10）g/100r流量可調(diào)；
●貯料斗容積：大于5L；
●試驗時間：可預(yù)置，數(shù)字顯示；
●砝碼一：一質(zhì)量為2.5㎏（適用GB/T3810.7-2006）；
●砝碼二：一質(zhì)量為14㎏（適用GB/ T12988-91）。
Fourth, ceramic wear tester technical parameters
● Grinding wheel one: diameter 200 ± 0.2mm, thickness 10 ± 0.1mm,
● Grinding wheel two: diameter 200 ± 0.2mm, thickness 70 ± 0.1mm, hardness HB203-245
● Wheel speed: 75 ± 4r / min constant;
● Sample size: 100mm × 110 mm;
● Abrasive: particle size is F80 white fused alumina specified in ISO8486-1986;
● Abrasion feeding speed: (100 ± 10) g / 100r flow rate adjustable;
● Storage hopper volume: greater than 5L;
● Test time: presettable and digital display;
● Weight one: one weight is 2.5㎏ (applicable to GB / T3810.7-2006);
● Weight two: one weight is 14㎏ (applicable to GB / T12988-91).
五、陶瓷耐磨試驗機注意事項及其保養(yǎng)：
●接通電源線時，應(yīng)注意電機正反轉(zhuǎn)，鋼輪應(yīng)該按照箭頭指示方向旋轉(zhuǎn)；
●試驗機必須在接**志處可靠接地（線徑不小于1.5mm）；
●每次試驗后，應(yīng)將試驗機打掃干凈，尤其應(yīng)將夾具及其導(dǎo)軌上的沙子清理干凈；
●每一年應(yīng)將齒輪箱側(cè)蓋板卸下，在齒輪上加適量鋰基潤滑脂。
●環(huán)境溫度：室溫
●周圍無腐蝕性性質(zhì)
●地面堅固水平
●電源為380V，電壓波動范圍不超過額定電壓的10%
Fifth, precautions and maintenance of ceramic wear tester
● When connecting the power cord, pay attention to the motor's forward and reverse rotation, and the steel wheel should rotate in the direction indicated by the arrow;
● The testing machine must be reliably grounded at the grounding mark (wire diameter is not less than 1.5mm);
● After each test, the test machine should be cleaned, especially the sａnd on the fixture and its guide rails;
● Remove the side cover of the gear box every year and add an appropriate amount of lithium-based grease to the gear.
● Ambient temperature: room temperature
● No corrosive nature around
● Sturdy ground level
● The power supply is 380V, and the voltage fluctuation range does not exceed 10% of the rated voltage